Laminated windshield with improved innerlayer

ABSTRACT

Safety glass is made by laminating to a ply of glass a saturated polyvinyl acetal film incorporating a photoinitiator. The exposed surface of the film is irradiated with ultraviolet light which activates the photoinitiator which in turn initiates crosslinking of the polymer. The polymer film retains its desirable mechanical and optical properties while the crosslinked surface has improved solvent-abrasion resistance.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation-in-part of application Ser. No. 793,674 entitled "Laminated Windshield with Improved Innerlayer," filed May 4, 1977 now U.S. Pat. No. 4,109,055, issued Aug. 22, 1978, which in turn is a division of application Ser. No. 682,538 entitled "Laminated Windshield with Improved Innerlayer," filed May 3, 1976, now U.S. Pat. No. 4,039,720, issued Aug. 2, 1977.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates broadly to the art of making safety glass and more particularly to the art of making safety glass windshields combining improvements in safety performance and optical quality durability.

2. Description of the Prior Art

Safety glass is a well-known term describing a glass-plastic laminate designed to reduce the severity of lacerative injuries resulting from impact sufficient to break the glass. A plastic film is laminated to a glass sheet so that upon impact sufficient to break the glass, the film adheres to the glass fragments, thus minimizing their dispersion. To be useful as safety glass, a laminate must have the following properties over a wide range of temperature and moisture conditions: (1) high energy absorption to minimize concussive injuries on impact, (2) high shear and tear strength to prevent rupture of the film by glass fragments, (3) sufficient adhesion between the layers to minimize dispersion of glass fragments thereby reducing the potential for lacerative injury, and (4) good optical quality.

Safety glass commercially employed is commonly a multiple laminate of two plies of glass with an interlayer of polyvinyl butyral plastic film. Alternative safety glass laminates, particularly for use as automobile windshields, are proposed either in the form of a single ply of glass with a plastic innerlayer or in the form of standard commercial safety glass with a plastic innerlayer on the inboard ply of glass. Upon impact sufficient to break these alternative forms of windshields, the probability of encountering glass fragments inside the passenger compartment is reduced. However, since the innerlayer will be exposed, the demands on the plastic film are much greater. It must not only meet the requirements of energy absorption, tear strength, adherence and optical quality previously discussed, but its surface must also have good weathering properties, chemical stability and abrasion resistance to provide durability for its required optical quality.

Thermoset polymer films typically have such durability; however, such films are difficult to laminate. In addition, rigid films contribute to concussive injury. Thermoplastic polymer films are relatively easy to laminate and are sufficiently ductile to absorb energy on impact, but they are often moisture and solvent sensitive and their surfaces are easily scratched, resulting in a loss of optical transparency.

It is known in the polymer art that some thermoplastic polymers, if crosslinked, become less elastomeric, less soluble, and in many respects similar to thermoset polymers. Thermoplastic polymers may be crosslinked during the polymerization reaction. However, crosslinked polymers are difficult to process. Alternatively, a polymer formulation may be treated with a crosslinking agent which can be activated subsequent to forming the polymer into the desired shape. Photochemical activation of a photosensitive crosslinking agent is an example.

The photochemical properties of benzophenone are well-known. For example, when exposed to ultraviolet radiation, such as sunlight, benzophenone in solution in an organic medium such as isopropanol, produces tetraphenylethylene glycol. The reaction mechanism consists of the following sequence of steps: ##STR1##

Excited benzophenone molecules are equally capable of abstracting hydrogen from hydrocarbons. The well-known oxidative dimerization of aliphatic hydrocarbons by photochemical reaction with benzophenone proceeds as follows: ##STR2##

A method for decreasing the thermoplasticity and solubility of polymers of ethylene usable as safety glass interlayers is taught by Roedel in U.S. Pat. No. 2,484,529. The method involves blending such polymers with ketones such as acetone, benzophenone or benzoin, and then exposing the blend to ultraviolet light.

An improved method for making polyethylene articles is taught by Tocker in U.S. Pat. No. 3,214,492. The method involves copolymerizing ethylene with acryloxy- or methacryloxy- substituted benzophenones or acetophenones, shaping the copolymer into a useful article, and exposing the article to ultraviolet radiation to produce crosslinking.

In U.S. Pat. No. 3,219,566, Potts et al teach that anthrone is superior to benzophenone for crosslinking polyethylene and polypropylene in the presence of ultraviolet light.

A method for making crosslinkable polyesters is taught in U.S. Pat. No. 3,518,175 to Bell. The method involves copolymerizing the polyester with a substituted benzophenone. Exposure of the resulting photosensitized terpolymer to ultraviolet radiation produces crosslinking.

In U.S. Pat. No. 2,929,710, Martin discloses polyvinyl acetal films containing initiators activatable by light of wavelengths from 1800 to 7000 Angstroms. The polyvinyl acetals of Martin's invention always contain a plurality of vinylidene groups in conjugative double bond systems.

It is not shown or suggested in the polymer art that saturated polyvinyl acetals, that is, polyvinyl acetals without extralinear vinylidene groups, are likewise crosslinkable by exposure to ultraviolet light in the presence of a photoinitiator such as benzophenone to produce a transparent layer that is crosslinked in at least a surface portion to improve its solvent-abrasion resistance without degrading its desired mechanical, adhesive and optical properties so that the polymer may be employed as an exposed innerlayer in a safety glass laminate.

SUMMARY OF THE INVENTION

The present invention provides an improved safety glass by combining the desirable properties of both thermoplastic and thermoset polymers in an innerlayer of thermoplastic polymer with its exposed surface crosslinked. The present invention further provides a method for making safety glass by laminating a saturated polyvinyl acetal layer to glass while the polymer is essentially thermoplastic, then crosslinking the exposed surface of the polymer to impart characteristics to the surface that improve the durability of its optical quality.

The present invention concerns saturated polyvinyl acetal films which can be laminated to a glass ply and subsequently crosslinked to produce more durable bilayer safety glass. For the purpose of discussing the present invention, glass ply is defined as a rigid transparent substrate which may include, in addition to glass, generally recognized glass substitutes such as acrylics, polycarbonates and other rigid, transparent plastics.

A crosslinkable polymer film is prepared by incorporating a small amount of photoinitiator, such as benzophenone or xanthone, into the polyvinyl acetal. The photoinitiator may be physically blended with the polymer before film formation or subsequently incorporated into the film, such as by soaking the film in a solution of the photoinitiator in an appropriate solvent or spraying the film with such a solution of the photoinitiator. Photoinitiators, for the purpose of carrying out the present invention, are chemical compounds which generate free radicals upon exposure to actinic radiation and initiate crosslinking of the polymer.

A thin film of crosslinkable polymer may be cast or extruded and laminated by conventional techniques to a glass ply. Alternatively, a film may be cast in place on the glass ply. The laminate is then exposed to ultraviolet radiation which activates the photoinitiator, which, in turn, initiates the crosslinking of the polymer, primarily at the exposed surface.

The desirable mechanical and optical properties of the film are retained while the solvent-abrasion resistance of the surface of the film is so improved by crosslinking that a safety glass laminate may be produced and used with the crosslinked polymer surface exposed.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

The polymers most useful in the practice of the present invention are saturated polyvinyl acetals prepared by the reaction of a polyhydric alcohol, a polyvinyl alcohol, with a saturated aldehyde. The resultant polyvinyl acetal does not contain extralinear vinylidene (--CH₂ ═ C<) groups which provide unsaturated sites for crosslinking by well-known methods.

The saturated polyvinyl acetal thus prepared may be blended with a photoinitiator and cast as a thin transparent film. Alternatively, the polyvinyl acetal may be cast or extruded as a thin transparent film and then soaked in or sprayed with a solution of a photoinitiator. Preferred photoinitiators include benzophenone, xanthone, acetophenone, anthraquinone, 2-methyl anthraquinone, 2[2'-hydroxy 5'-methylphenyl] benzotriazole, anthrone and butanedione. Benzophenone and xanthone are most preferred. Less preferred are photoinitiators which have a tendency to discolor the polymer with age, notably anthrone. The preferred range of photoinitiator concentration is from about 0.3 to about 5 percent based on the weight of the polymer. The optimum concentration depends on the choice of photoinitiator and the duration of exposure to ultraviolet light.

The crosslinkable polymer film is laminated, preferably by pressing the film between two glass plies, one of which is coated with a release agent such as a polysiloxane or polytetrafluoroethylene (TEFLON®), and heating to promote adhesion of the film to the uncoated glass ply. A detailed description of a preferred laminating technique is found in U.S. Pat. No. 3,808,077 to Rieser et al., which description is incorporated herein by reference. Alternatively, the polymer may be cast in place by a technique such as that described in U.S. Pat. No. 3,509,015 to Wismer et al. In this method, film forming and laminating are accomplished in one operation.

Following lamination, the free surface of the film is exposed to actinic radiation, preferably ultraviolet radiation in the wavelength range of 200 to 400 nanometers, until sufficient crosslinking has occurred to render the surface substantially more solvent-abrasion resistant than an untreated surface.

The laminates thus produced are particularly useful as windshields, sidelights and backlights, in automobiles and other vehicles. For optimum safety performance, the preferred laminate comprises 3/32 to 3/16 inch (2.3 to 4.5 millimeter) thick glass ply and a 15 to 40 mil (0.4 to 1.0 millimeter) thick polymer film.

The present invention will be further understood from the descriptions of specific examples which follow. The substrate used in the example as 1/8 inch (3 millimeter) thick soda-lime-silica float glass. The film is laminated to the substrate by assembling the film between two plies of glass, one of which is coated with a release agent, placing the assembly in a plastic bag, evacuating and sealing the bag, and placing the bagged assembly in an oil autoclave at a temperature of about 300° F. (about 149° C.) and pressure of about 200 pounds per square inch (about 1.38 × 10⁶ newtons per square meter) for about 45 minutes. The laminate is then irradiated by lamps which produce ultraviolet radiation predominantly in the range of from 300 to 380 nanometers.

Following ultraviolet treatment, the exposed polymer surface is abraded with 400 mesh synthetic alundum abrasive and acetone by 1000 passes of a one pound (454 gram) weighted felt pad. The solvent abrasion resistance of the surface is then determined by dividing a 1.5 inch (38.1 millimeter) square in the center of a 2 inch by 4 inch (about 50 millimeter by 100 millimeter) sample into nine areas and measuring the percent haze in the central portion of each area. The haze values reported herein are the averages of the nine individual area haze measurements for each sample. The percent haze is measured on a Gardner Automatic Pivotable Sphere Hazemeter with back-lighting and an illuminant "C" Filter. The solvent abrasion resistances of the samples described in Examples I through IX, as measured by the percent haze after acetone-abrasion, are compared in Table I. The samples were further tested to determine their safety performance characteristics and were found to be acceptable according to commercial standards for automotive safety glass and comparable to bilayer laminates of glass and uncrosslinked polymer. Impact performance data for Examples XI and XII are compared in Table II. The following examples are offered to illustrate the invention.

EXAMPLE I

A polyurethane composition is prepared by reacting 4,4'-methylene-bis-(cyclohexyl isocyanate), a hydroxy-terminated polybutylene adipate diol having a molecular weight of about 2000, and 1,4 butanediol in a mole ratio of about 3.71:1.00:2.71 for about 24 hours at about 290° F. (about 143° C.). The polyurethane is extruded by conventional technique as a 20 mil (0.5 millimeter) thick film. Four inch (100 millimeter) square portions of the polyurethane film are laminated to glass substrates. An untreated, unabraded laminate has 3.0 percent haze. A laminate is cut into 2 by 4 inch (about 50 by 100 millimeter) samples which are abraded with 400 mesh synthetic alundum abrasive and acetone by 1000 passes of a one pound (454 grams) weighted felt pad. The abraded samples have an average of 8.1 percent haze.

EXAMPLE II

A laminate as described in Example I is then cut into two 2 by 4 inch (50 by 100 millimeters) samples which are irradiated with ultraviolet radiation (UV), one for 15 minutes and the other for 60 minutes. The exposed film surfaces of the laminates are then abraded as in Example I. After such solvent-abrasion, the samples show 11.7 and 13.6 percent haze.

EXAMPLE III

A polyurethane film as described in Example I is soaked in methyl ethyl ketone (MEK) for 45 minutes at room temperature. The film is then dried and laminated to a glass substrate. Two 2 by 4 inch (50 by 100 millimeter) samples of the laminate are then exposed to ultraviolet radiation and subjected to solvent-abrasion treatment as in Example II. The samples show 13.6 and 8.9 percent haze.

EXAMPLE IV

A polyurethane film as described in Example I is soaked for 45 minutes at room temperature in a solution of 5 percent benzophenone in MEK. The film is dried and laminated as in Example III, and exposed to ultraviolet radiation for 15 minutes. Following the solvent-abrasion treatment as in the previous examples, the sample shows only 3.5 percent haze.

EXAMPLE V

A sample is prepared as in Example IV accept that the MEK soak solution contains 2.5 percent benzophenone and the laminate is exposed to ultraviolet radiation for 60 minutes. After solvent-abrasion as in the previous examples, the sample shows 4.8 percent haze.

EXAMPLE VI

A sample is prepared as in Example IV except that the MEK soak solution contains 0.6 percent xanthone in place of benzophenone. The abraded sample has 4.0 percent haze.

EXAMPLE VII

A sample is prepared as in Example V except that the MEK solution contains 5 percent acetophenone in place of benzophenone. Following solvent-abrasion as in the previous examples, the sample shows 5.1 percent haze.

EXAMPLE VIII

Polyurethane prepared as in Example I is blended with 1.5 percent benzophenone and pressed into a transparent sheet. The sheet is laminated to a glass substrate and exposed to ultraviolet radiation for one hour. After solvent-abrasion as in Example I, the sample has 3.3 percent haze.

EXAMPLE IX

Polyurethane is prepared by reacting 4,4'-methylene-bis(cyclohexyl isocyanate), a hydroxy terminated polycaprolactone diol of molecular weight about 1,000 and 1,4 butanediol in a mole ratio of about 2.3:1.0:1.3. The polyurethane is then physically blended with 1.5 percent by weight benzophenone. A film is cast and laminated to a glass substrate. The sample is exposed to ultraviolet radiation for one hour. After solvent-abrasion as in Example I, the sample has 4.7 percent haze.

EXAMPLE X

Polyurethane is prepared as in Example I and extruded as a 0.020 inch (about 0.5 millimeter) film. Portions of the film are sprayed with a solution of 5 percent by weight benzophenone in methyl ethyl ketone. The films are then dried for 15 minutes at 200° F. (about 93° C.). The films contain about 3.6 percent by weight benzophenone. Portions of the films are then laminated to 7/32 inch (about 5.6 millimeter) thick float glass plies. The laminates are exposed to ultraviolet radiation for at least 30 minutes. After solvent-abrasion as in Example I the samples show only light, very light, little or no abrasion.

EXAMPLE XI

In order to show that the improvement in solvent-abrasion resistance was not obtained at the expense of safety performance, untreated polyurethane films as described in Example I are laminated to 12 by 12 inch (about 300 by 300 millimeter) plies of glass. The resulting laminates are held rigid in a frame and impacted from the film side with a 5 pound (2.27 kilogram) freely falling steel ball. The velocity of the ball at impact is calculated from the height at which the ball is released. The height is increased until the velocity of the ball is sufficient to penetrate the laminate. The penetration velocities for the uncrosslinked laminates are 20.3 miles per hour at 0° F. (about -18° C.), 19.9 miles per hour at 70° F. (about 21° C.) and 15.1 miles per hour at 120° F. (about 49° C.).

EXAMPLE XII

For comparison with the uncrosslinked samples of Example XI, polyurethane films as described in Example I are soaked for one hour in a 5 percent by weight solution of benzophenone in methyl ethyl ketone. The films are dried and laminated to 12 by 12 inch (about 300 by 300 millimeter) glass substrates and then exposed to ultraviolet radiation for 30 minutes. The resulting laminates are held rigid in a frame and impacted as in Example XI. The penetration velocities for the crosslinked laminates are 21.7 miles per hour at 0° F. (about -18° C.), 18.4 miles per hour at 70° F. (about 21° C.) and 15.1 miles per hour at 120° F. (about 49° C.).

                  TABLE I                                                          ______________________________________                                         Solvent-Abrasion Resistance of Polyurethane Innerlayer                                                       UV Exposure                                                                             Haze                                    Example Photoinitiator                                                                             Solution  (minutes)                                                                               (%)                                     ______________________________________                                         I       none        none      none     3.0*                                            none        none      none     8.1                                     II      none        none      15       11.7                                            none        none      60       13.6                                    III     none        MEK       15       13.6                                            none        MEK       60       8.9                                     IV      5% BP       MEK       15       3.5                                     V       2.5% BP     MEK       60       4.8                                     VI      0.6% X      MEK       15       4.0                                     VII     5% AP       MEK       60       5.1                                     VIII    1.5% BP     none      60       3.3                                     IX      1.5% BP     none      60       4.7                                     ______________________________________                                          *Unabraded                                                                     MEK - methyl ethyl ketone                                                      BP - benzophenone                                                              X - xanthone                                                                   AP - acetophenone                                                        

                  TABLE II                                                         ______________________________________                                         Penetration Resistance of Polyurethane Innerlayer                                              Penetration Velocity of Laminate                                              (miles per hour)                                                Example  Innerlayer  0° F.                                                                            70° F.                                                                          120° F.                           ______________________________________                                         X        Uncrosslinked                                                                              20.3     19.9    15.7                                     XI       Crosslinked 21.7     18.4    15.1                                     ______________________________________                                    

Although the present invention has been described in detail with respect to bilayer glass laminates, the scope of the invention is not limited thereto. It will be evident to persons skilled in the art that variations and modifications may be made without departing from the spirit of this invention. For example, commonly known glass substitutes such as polycarbonates and acrylics may be used in place of glass. The glass ply may be the inboard ply of a conventional trilayer windshield. Thermoplastic polyvinyl acetals, especially polyvinyl butyral, may be used as the crosslinkable polymer. Known photoinitiators may be substituted for the preferred photoinitiators. Other appropriate solvents for the photoinitiators may be employed, or the film may be exposed to photoinitiator in vapor form. The polymer film may also incorporate additional components such as adhesion control additives. These and other variations will become obvious in the light of the claimed subject matter that follows. 

We claim:
 1. A transparent polymer film for use as an innerlayer in a bilayer safety glass laminate which consists essentially of a saturated thermoplastic polyvinyl acetal and an effective amount of a photoinitiator capable of initiating crosslinking of said film upon exposure to actinic radiation.
 2. A film as described in claim 1, wherein the photoinitiator is selected from the group consisting of benzophenone, xanthone, acetophenone, anthraquinone, 2[2'-hydroxy 5'-methylphenyl] benzotriazole, anthrone, and butanedione.
 3. A film as described in claim 2, wherein said photoinitiator is benzophenone.
 4. A film as described in claim 2, wherein said photoinitiator is xanthone. 